Santoprene TPV Encapsulated 316L Chemical Injection Line

Short Description:

The engineering disciplines involved in flow assurance play an essential part in mapping the requirements that reduce or prevent loss of production due to pipeline or process equipment blockage. Coiled tubing from Meilong Tube is applied to umbilicals and chemical injection systems play an effective role in chemical storage and delivery at an optimizing flow assurance.

Send email to us

Product Detail

Product Tags

Typical Tubing Size

Imperial size		Metric size
OD inch	WT inch	OD mm	WT mm
1/8 (0.125)	0.028	3.18	0.71
1/8 (0.125)	0.035	3.18	0.89
3/16 (0.188)	0.028	4.76	0.71
	0.035	4.76	0.89
	0.049	4.76	1.24
1/4 (0.250)	0.035	6.35	0.89
	0.049	6.35	1.24
	0.065	6.35	1.65
	0.083	6.35	2.11
3/8 (0.375)	0.035	9.53	0.89
	0.049	9.53	1.24
	0.065	9.53	1.65
	0.083	9.53	2.11
1/2 (0.500)	0.035	12.7	0.89
	0.049	12.7	1.24
	0.065	12.7	1.65
	0.083	12.7	2.11

Product Display

Santoprene TPV Encapsulated 316L Chemical Injection Line (3)

Santoprene TPV Encapsulated 316L Chemical Injection Line (2)

Alloy Feature

Caustic Environments

Austenitic steels are susceptible to stress corrosion cracking. This may occur at temperatures above about 60°C (140°F) if the steel is subjected to tensile stresses and at the same time comes into contact with certain solutions, particularly those containing chlorides. Such service conditions should therefore be avoided. Conditions when plants are shut down must also be considered, as the condensates which are then formed can develop conditions that lead to both stress corrosion cracking and pitting.

SS316L has a low carbon content and therefore better resistance to intergranular corrosion than steels of type SS316.

Encapsulation Features

Maximize protection of downhole line

Increase crush resistance during installation

Protect injection line against abrasion and pinching

Eliminate long term stress corrosion failure of control line

Improve clamping profile

Single or multiple encapsulation for ease of running and added protection

Technical Datasheet

Alloy	O.D.	W.T.	Yield Strength	Tensile Strength	Elongation	Hardness	Working Pressure	Burst Pressure	Collapse Pressure
	inch	inch	Mpa	Mpa	%	HV	psi	psi	psi
			min.	min.	min.	max.	min.	min.	min.
SS316L	0.375	0.035	172	483	35	190	3,818	17,161	5,082
SS316L	0.375	0.049	172	483	35	190	5,483	24,628	6,787
SS316L	0.375	0.065	172	483	35	190	7,517	33,764	8,580
SS316L	0.375	0.083	172	483	35	190	9,749	43,777	10,357